Effect of Compaction Pressure on Sintered Properties of Synthesized Al6061 Alloys through Powder Metallurgy Route |
Author(s): |
| Md Alamgir , A.M.U-Aligarh U.P, India |
Keywords: |
| Al6061, Wear Rate, Hardness, Ball Milling, Sintering, Density, XRD |
Abstract |
|
Recently Aluminium alloy, exclusively Al6061 is used in the automotive, aircraft, marine and construction industries due to it is excellent properties such as noncorrosive, strength to weight ratio and rewards over than steel in ductility. In this study Al6061 was produced by mechanical powder metallurgy. Three value of compaction pressure (300,340,380MPa) were taken for centrifugal Ball milling of 45 minute with BPR 10:1, sintering is done at 450 0C for 30 minute in tubular electric furnace in the controlled atmosphere of Argon gas. The Scanning Electron Microscope (SEM) was done to see the morphology of the compacts. Green, sintered density and XRD was also calculated. |
Other Details |
|
Paper ID: IJSRDV5I70441 Published in: Volume : 5, Issue : 7 Publication Date: 01/10/2017 Page(s): 932-934 |
Article Preview |
|
|
|
|